Study the Frequency Dependence of Dielectric Properties of Gamma Irradiated PVA(1-x)PSx Polymer Blends

PVA(1-x)PSx (x = 0.0, 0.25, 0.50, 0.75 and 1.0) polymer blend films were prepared by simple solution cast method using mixer of dimethyl sulphoxide (DMSO) and double distilled water (DDW) as a common solvent. Gamma irradiation studies have been carried out to investigate the potential for improvements in the electrical properties of pure and blend polymer film. The induced changes in the dielectric constant (εr), dielectric loss (tanδ) and AC conductivity (σac) properties for the unirradiated and irradiated films were studied, in the frequency range 50 Hz – 5 MHz at room temperature (27°C). Further, it was seen that the frequency dependent dielectric constant, dielectric loss and AC conductivity were found to increase with increasing γ irradiation dose for all the PVA(1-x)PSx (x = 0.0, 0.25, 0.50, 0.75 and 1.0) polymer blends. The maximum σac at 1 kHz frequency was observed to be 2.4421 × 10-6 s/m (at room temperature) for PVA film irradiated at 1.5 kGy.

来源: Study the Frequency Dependence of Dielectric Properties of Gamma Irradiated PVA(1-x)PSx Polymer Blends

Advertisements

发表评论

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / 更改 )

Twitter picture

You are commenting using your Twitter account. Log Out / 更改 )

Facebook photo

You are commenting using your Facebook account. Log Out / 更改 )

Google+ photo

You are commenting using your Google+ account. Log Out / 更改 )

Connecting to %s